Авторы
Zinin, P. V.
Bulatov, K. M.
Filonenko, V. P.
Fominski, V. Y.
Romanov, R. I.
Vasil'evskii, I. S.
Safonov, D. A.
Soloviev, A. A.
Показать ещё 3
Journal Title
Journal ISSN
Volume Title
Издатель
Научные группы
Организационные подразделения
OrgUnit Logo
Организационная единица
Институт лазерных и плазменных технологий
Стратегическая цель Института ЛаПлаз – стать ведущей научной школой и ядром развития инноваций по лазерным, плазменным, радиационным и ускорительным технологиям, с уникальными образовательными программами, востребованными на российском и мировом рынке образовательных услуг.
OrgUnit Logo
Организационная единица
Институт нанотехнологий в электронике, спинтронике и фотонике
Институт ИНТЭЛ занимается научной деятельностью и подготовкой специалистов в области исследования физических принципов, проектирования и разработки технологий создания компонентной базы электроники гражданского и специального назначения, а также построения современных приборов на её основе. ​Наша основная цель – это создание и развитие научно-образовательного центра мирового уровня в области наноструктурных материалов и устройств электроники, спинтроники, фотоники, а также создание эффективной инновационной среды в области СВЧ-электронной и радиационно-стойкой компонентной базы, источников ТГц излучения, ионно-кластерных технологий материалов.​
Выпуск журнала
Аннотация
© 2019 Elsevier B.V. Relatively low and high deposition rates of BCх films were realized by pulsed laser ablation of mixed B–diamond and dual B–graphite targets, respectively. Deposition was performed at 500 °C and the rate of film deposition was determined with respect to the number of atomic monolayers (obviously less or more than one monolayer) grown for one laser pulse. In the case of BCх films formation with a low deposition rate, doping with B facilitated the growth of the nanocomposite structure, which possessed an increased fraction of sp3 bonds, a very low electrical resistance, and an improved mechanical performance. The change of the sheet resistance of these films as the temperature was reduced from 300 to 65 K had a metallic character. For about 95-nm-thick films with bulk compositions of BC1.7 and BC0.6, the resistivity at room temperature were approximately equal to 1.5 mΩ·cm, and the lowest resistivity of 0.23 mΩ·cm was detected for B-enriched film at 85 K. With an increase in the B atom concentration in such films, the charge carrier (holes) concentration decreased, and their mobility increased from 180 to 10,500 cm2·V−1·s−1 due to samples cooling. The application of a higher deposition rate from the dual B–graphite target activated surface migration of condensed atoms, which caused the development of granular morphology, the B segregation and the reduction of the sp3 bond fraction. The hardness and electrical conductivity of such films were obviously inferior to those of the films obtained by PLD with a low deposition rate.
Описание
Ключевые слова
Цитирование
Structural, electrical and mechanical properties of ВСх films prepared by pulsed laser deposition from mixed and dual boron-diamond/graphite targets / Zinin, P.V. [et al.] // Diamond and Related Materials. - 2019. - 92. - P. 266-277. - 10.1016/j.diamond.2018.12.026
URI
https://www.doi.org/10.1016/j.diamond.2018.12.026
 https://www.scopus.com/record/display.uri?eid=2-s2.0-85059565041&origin=resultslist
 http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcAuth=Alerting&SrcApp=Alerting&DestApp=WOS_CPL&DestLinkType=FullRecord&UT=WOS:000461129800035
 https://openrepository.mephi.ru/handle/123456789/16443
Коллекции
Публикации