Publication:
Precipitation kinetics of radiation-induced Ni-Mn-Si phases in VVER-1000 reactor pressure vessel steels under low and high flux irradiation

Дата
2021
Авторы
Zhuchkov, G. M.
Fedotova, S. V.
Maltsev, D. A.
Frolov, A. S.
Kuleshova, E. A.
Journal Title
Journal ISSN
Volume Title
Издатель
Научные группы
Организационные подразделения
OrgUnit Logo
Организационная единица
Институт ядерной физики и технологий
Цель ИЯФиТ и стратегия развития - создание и развитие научно-образовательного центра мирового уровня в области ядерной физики и технологий, радиационного материаловедения, физики элементарных частиц, астрофизики и космофизики.
Выпуск журнала
Аннотация
© 2021One of the key embrittlement mechanisms in reactor pressure vessel (RPV) steels is the hardening produced by nanometer features. In this paper low Cu high Ni VVER-1000 RPV steels with a wide range of Ni (1.1–1.94wt.%) and Mn (0.38–1.1wt.%) contents irradiated at 290°C to (6–101) 1022 n/m22 (E>0.5MeV) at both low (surveillance specimens) and high (test reactor) fluxes were analyzed using atom probe tomography and transmission electron microscopy. Formation of high number density of NMS precipitates with the average composition close to at.%: 45Ni-33Si-22Mn regardless of the irradiation conditions was observed. Its number density increases with the increase of the total Ni and Mn concentration in steel. High flux irradiation demonstrates lower size and volume fraction of NMS precipitates compared to the low flux irradiation in case of welds. For the base metal specimens with low Ni (1.1–1.3 wt.%) and Mn (0.38–0.51) content no flux effect was observed. The contribution of NMS phases and dislocation loops into radiation hardening of RPV steels was established by the dispersed barrier strength model (Orowan equation).
Описание
Ключевые слова
Цитирование
Precipitation kinetics of radiation-induced Ni-Mn-Si phases in VVER-1000 reactor pressure vessel steels under low and high flux irradiation / Zhuchkov, G.M. [et al.] // Journal of Nuclear Materials. - 2021. - 553. - 10.1016/j.jnucmat.2021.153091
URI
https://www.doi.org/10.1016/j.jnucmat.2021.153091
 https://www.scopus.com/record/display.uri?eid=2-s2.0-85107152500&origin=resultslist
 http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcAuth=Alerting&SrcApp=Alerting&DestApp=WOS_CPL&DestLinkType=FullRecord&UT=WOS:000663795100011
 https://openrepository.mephi.ru/handle/123456789/25525
Коллекции
Публикации